Effects of heat treatments and applied loads on the tribological behavior of Ti-56.5 wt. % Ni and Ti-57.5 wt. % Ni alloys were investigated. Wear tests were performed on a pin-on-disk tribometer under normal loads of 20 N and 60 N at a sliding speed of 0.3 m/s. The results indicated that the alloys aged at 700 °C showed lower hardness comparing to the alloys aged at 400 °C. Under an applied load of 20 N, the samples aged at 700 °C showed better wear behavior in comparison with the samples aged at 400 °C with a higher hardness. This could be attributed to higher toughness of the samples aged at 700 °C. The results also showed that the wear of the samples aged at 400 °C decreased with the increase in normal load. However, there was an increase in the wear of the samples aged at 700 °C with the increase of load. Formation and stability of tribological layers on the contacting surfaces could be the main reason for the reduction of the wear of the samples aged at 400 °C with the increase in normal load.
Skip Nav Destination
e-mail: hghasemi@ut.ac.ir
Article navigation
July 2011
Research Papers
Tribological Behavior of Heat Treated Ni-rich NiTi Alloys
R. Aliasgarian,
R. Aliasgarian
School of Metallurgy and Materials Engineering,
University of Tehran
, P.O. Box 11155-4563, Tehran, Iran
Search for other works by this author on:
H. M. Ghasemi,
H. M. Ghasemi
School of Metallurgy and Materials Engineering,
e-mail: hghasemi@ut.ac.ir
University of Tehran
, P.O. Box 11155-4563, Tehran, Iran
Search for other works by this author on:
M. Abedini
M. Abedini
School of Metallurgy and Materials Engineering,
University of Tehran
, P.O. Box 11155-4563, Tehran, Iran
Search for other works by this author on:
R. Aliasgarian
School of Metallurgy and Materials Engineering,
University of Tehran
, P.O. Box 11155-4563, Tehran, Iran
H. M. Ghasemi
School of Metallurgy and Materials Engineering,
University of Tehran
, P.O. Box 11155-4563, Tehran, Iran
e-mail: hghasemi@ut.ac.ir
M. Abedini
School of Metallurgy and Materials Engineering,
University of Tehran
, P.O. Box 11155-4563, Tehran, Iran
J. Tribol. Jul 2011, 133(3): 031602 (6 pages)
Published Online: July 12, 2011
Article history
Received:
August 26, 2010
Revised:
April 11, 2011
Online:
July 12, 2011
Published:
July 12, 2011
Citation
Aliasgarian, R., Ghasemi, H. M., and Abedini, M. (July 12, 2011). "Tribological Behavior of Heat Treated Ni-rich NiTi Alloys." ASME. J. Tribol. July 2011; 133(3): 031602. https://doi.org/10.1115/1.4004102
Download citation file:
Get Email Alerts
Cited By
Related Articles
Effect of Phase Transformation on the Wear Behavior of NiTi Alloy
J. Eng. Mater. Technol (July,2010)
Effect of Heat Treatment and Electric Discharge Alloying on the Tribological Performance of Selective Laser Melted AlSi10Mg
J. Tribol (May,2021)
Scratch and Sliding Wear Testing of Electroless Ni–B–W Coating
J. Tribol (February,2020)
Related Proceedings Papers
Related Chapters
The Tribological Character of LB Films of Dipalmitoylphosphatidylcholine (DPPC)
International Conference on Mechanical and Electrical Technology, 3rd, (ICMET-China 2011), Volumes 1–3
Systematic Testing of Ceramic Rolling Bearing Elements
Selection and Use of Wear Tests for Ceramics
Wet-Sand Rubber-Wheel Abrasion Test for Thin Coatings
Selection and Use of Wear Tests for Coatings