The dependence of the nanotribological properties of ultrathin amorphous carbon (a-C) films, deposited on Si(100) substrates by radio frequency sputtering, on their nanomechanical properties was investigated using surface force microscopy. The thickness and nanohardness of the a-C films were found to be in the range of 7–95 nm and 9–44 GPa, respectively. Sharp conical diamond tips with a 90 deg included angle and radius of curvature of about 20 μm and 100 nm were used to perform friction and wear experiments, respectively. The effect of the substrate compliance on the nanomechanical and nanotribological properties of the a-C films is interpreted in terms of the indentation depth and the film thickness. The coefficient of friction and wear rate of the a-C films are related to their nanomechanical properties, thickness, and surface roughness. The dependence of the coefficient of friction on contact load and the dominant friction mechanisms of elastically and plastically deformed films are discussed in light of friction force and surface imaging results. High effective hardness-to-elastic modulus ratio and low surface roughness characterize high wear resistance a-C films. Below a critical load, the steady-state removal rate of the film material is insignificantly small, revealing a predominantly elastic behavior.
Skip Nav Destination
Article navigation
July 2001
Technical Papers
Nanotribological and Nanomechanical Properties of Ultrathin Amorphous Carbon Films Synthesized by Radio Frequency Sputtering
W. Lu, Graduate Student,
W. Lu, Graduate Student
Fellow ASME Department of Mechanical Engineering, University of California, Berkeley, CA 94720
Search for other works by this author on:
K. Komvopoulos, Professor
K. Komvopoulos, Professor
Fellow ASME Department of Mechanical Engineering, University of California, Berkeley, CA 94720
Search for other works by this author on:
W. Lu, Graduate Student
Fellow ASME Department of Mechanical Engineering, University of California, Berkeley, CA 94720
K. Komvopoulos, Professor
Fellow ASME Department of Mechanical Engineering, University of California, Berkeley, CA 94720
Contributed by the Tribology Division for publication in the ASME JOURNAL OF TRIBOLOGY. Manuscript received by the Tribology Division May 1, 2000; revised manuscript received October 31, 2000. Associate Editor: Y.-W. Chung.
J. Tribol. Jul 2001, 123(3): 641-650 (10 pages)
Published Online: October 31, 2000
Article history
Received:
May 1, 2000
Revised:
October 31, 2000
Citation
Lu, W., and Komvopoulos, K. (October 31, 2000). "Nanotribological and Nanomechanical Properties of Ultrathin Amorphous Carbon Films Synthesized by Radio Frequency Sputtering ." ASME. J. Tribol. July 2001; 123(3): 641–650. https://doi.org/10.1115/1.1339977
Download citation file:
Get Email Alerts
Related Articles
Nanoscale Indentation Hardness and Wear Characterization of Hydrogenated Carbon Thin Films
J. Tribol (April,1996)
Nanoscale Indentation Hardness and Wear Characterization of Hydrogenated Carbon Thin Films
J. Tribol (October,1995)
Related Proceedings Papers
Related Chapters
Wear and Contact Fatigue Properties of a Novel Lubricant Additive
Bearing and Transmission Steels Technology
Understanding the Problem
Design and Application of the Worm Gear
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies