An AMTI knee simulator was used to evaluate the wear of UHMWPE tibial inserts which were gamma sterilized in air and displayed a high or low level of oxidation. After 5 million cycles, four out of five samples from the high oxidation group displayed subsurface cracking and/or delamination. The five specimens in the low oxidation group experienced burnishing only. These results indicate that gamma irradiation in air together with high oxidation due to shelf aging can increase susceptibility to wear. The appearance of the wear scars indicates that knee simulator testing is a valid method of producing burnishing, cracking, and delamination similar to that seen in-vivo. [S0742-4787(00)04301-0]

1.
Collier
,
J. P.
,
Sutula
,
L. C.
,
Currier
,
B. H.
,
Currier
,
J. H.
,
Wooding
,
R. E.
,
Williams
,
I. R.
,
Farber
,
K. B.
, and
Mayor
,
M. B.
,
1996
, “
Overview Of Polyethylene As A Bearing Material: Comparison Of Sterilization Methods
,”
Clin. Orthop. Relat. Res.
,
333
, pp.
76
86
.
2.
Gillis
,
A.
,
Furman
,
B.
,
Perone
,
J.
,
Lefebvre
,
F.
,
Reish
,
T.
, and
Li
,
S.
,
1997
, “
Oxidation of In Vivo Versus Shelf Life Aged Gamma Sterilized Total Knee Replacements
,”
Transactions of the Society for Biomaterials
, Society for Biomaterials, Minneapolis, MN,
20
, p.
73
73
.
3.
Li
,
S.
, and
Burstein
,
A. H.
,
1994
, “
Current Concepts Review: Ultra-High Molecular Weight Polyethylene
,”
J. Bone Jt. Surg.
,
76-A
, pp.
1080
1090
.
4.
Premnath
,
V.
,
Harris
,
W. H.
,
Jasty
,
M.
, and
Merrill
,
E. W.
,
1996
, “
Gamma Sterilization of UHMWPE Articular Implants: an Analysis of the Oxidation Problem
,”
Biomaterials
,
17
, pp.
1741
1753
.
5.
Collier
,
J. P.
,
Sperling
,
D. K.
,
Currier
,
J. H.
,
Sutula
,
L. C.
,
Saum
,
K. A.
, and
Mayor
,
M. B.
,
1996
, “
Impact of Gamma Sterilization on Clinical Performance of Polyethylene in the Knee
,”
Journal of Arthroplasty
,
11
, pp.
377
389
.
6.
Currier
,
B. H.
,
Currier
,
J. H.
,
Collier
,
J. P.
,
Mayor
,
M. B.
, and
Scott
,
R. D.
,
1997
, “
Shelf Life and In-vivo Duration
,”
Clin. Orthop. Relat. Res.
,
342
, pp.
111
122
.
7.
Greer, K. W., and Flynn, M. A., 1996, “Analysis of the Interrelationship Between Pitting Wear, Oxidation, Crystallinity, and Storage Time for Shelf Aged UHMWPE Implants,” Transactions of the 5th World Biomaterials Congress, University of Toronto Press, Toronto, Canada, 2, p. 190.
8.
Besong
,
A. A.
,
Tipper
,
J. L.
,
Ingham
,
E.
,
Stone
,
M. H.
,
Wroblewski
,
B. M.
, and
Fisher
,
J.
,
1998
, “
Quantitative Comparison of Wear Debris from UHMWPE that Has and Has Not Been Sterilized by Gamma Irradiation
,”
J. Bone Jt. Surg.
,
80-B
, pp.
340
344
.
9.
Fisher
,
J.
,
Chan
,
K. L.
,
Hailey
,
J. L.
,
Shaw
,
D.
, and
Stone
,
M.
,
1995
, “
Preliminary Study of the Effect of Aging Following Irradiation on the Wear of Ultrahigh-Molecular-Weight Polyethylene
,”
Journal of Arthroplasty
,
10
, pp.
689
692
.
10.
McKellop
,
H.
,
Clarke
,
I.
,
Markolf
,
K.
, and
Amstutz
,
H.
,
1981
, “
Friction and Wear Properties of Polymer, Metal, and Ceramic Prosthetic Joint Materials Evaluated on a Multichannel Screening Device
,”
J. Biomed. Mater. Res.
,
15
, pp.
619
653
.
11.
Wang
,
A.
,
Essner
,
A.
,
Polineni
,
V. K.
,
Stark
,
C.
, and
Dumbleton
,
J. H.
,
1998
, “
Lubrication and Wear of Ultra-High Molecular Weight Polyethylene in Total Joint Replacements
,”
Tribol. Int.
,
31
, pp.
17
33
.
12.
Bragdon, C. R., Jasty, M., Lowenstein, J. D., Elder, J., and Lee, K. R., 1996, “Mechanism of Wear in Retrieved Polyethylene Acetabular Components,” Proceedings, 63rd Annual Meeting, American Academy of Orthopaedic Surgeons, American Academy of Orthopaedic Surgeons, Rosemont, IL., Paper No. 376.
13.
Wang
,
A.
,
Polineni
,
V. K.
,
Essner
,
A.
,
Sokol
,
M.
,
Sun
,
D. C.
, and
Dumbleton
,
J. H.
,
1997
, “
The Significance of Nonlinear Motion in the Wear Screening of Orthopaedic Implant Materials
,”
J. Test. Eval.
,
25
, pp.
239
245
.
14.
McKellop
,
H.
,
Clarke
,
I.
,
Markolf
,
K.
, and
Amstutz
,
H.
,
1978
, “
Wear Characteristics of UHMW Polyethylene: A Method for Accurately Measuring Extremely Low Wear Rates
,”
J. Biomed. Mater. Res.
,
12
, pp.
895
927
.
15.
Mow, V. C., and Hayes, W. C., 1991, Basic Orthopaedic Biomechanics, Raven Press, New York, NY, pp. 54–88.
16.
Andriacchi
,
T. P.
,
Andersson
,
G. B.
,
Fermier
,
R. W.
,
Stern
,
D.
, and
Galante
,
J. O.
,
1980
, “
A Study of Lower-Limb Mechanics During Stair-Climbing
,”
J. Bone Jt. Surg.
,
62-A
, pp.
749
757
.
17.
Andriacchi
,
T. P.
,
Galante
,
J. O.
, and
Ferrnier
,
R. W.
,
1982
, “
The Influence of Total Knee Replacement Design on Walking and Stair-Climbing
,”
J. Bone Jt. Surg.
,
64-A
, pp.
1328
1335
.
18.
Hersh, J. F., 1980, “Laboratory Evaluation of Knee Prostheses,” MSME thesis, Department of Mechanical Engineering, Purdue University, West Lafayette, IN.
19.
Maletsky, L. P., and Hillberry, B. M., 1997, “Dynamic Control of a Four-Axis, Electrohydraulic Knee Simulator,” Proceedings of the ASME Dynamic Systems and Control Division, Vol. 61, pp. 447–452.
20.
Sheshadri, V. B., Rullkoetter, P. J., and Hillberry, B. M., 1997, “In Vitro Measurement of the Six Degree-of-Freedom Kinematics of the Human Knee During Simulated Gait,” Proceedings of the ASME Dynamic Systems and Control Division, Vol. 61, pp. 375–379.
21.
Maletsky, L., Benda, P., and Hillberry, B. M., 1995, “Knee Kinematic Analysis: Natural, Prostheses Implanted in Cadaver, and Prostheses Mounted in Fixtures,” Report to Johnson & Johnson Professional, Purdue University, West Layfayette, IN.
22.
McLeod
,
P. C.
,
Kettelkamp
,
D. B.
,
Srinivasan
,
V.
, and
Henderson
,
O. L.
,
1975
, “
Measurements of Repetitive Activities of the Knee
,”
J. Biomech.
,
8
, pp.
369
373
.
23.
Bragdon, C. R., O’Conner, D. O., Weinberg, E. A., Skehan, H., 3rd, Muratoglu, O. K. Lowenstein, J. D., and Harris, W. H., 1999, “The Effect of Cycle Rate on the Wear of Conventional and Highly Crosslinked UHMWPE Acetabular Components Using the Boston AMTI Hip Simulator,” Transactions of the 45th Annual Meeting of the Orthopaedic Research Society, Orthopaedic Research Society, Rosemont, IL, 24, p. 831.
24.
Fisher
,
J.
,
Dowson
,
D.
,
Hamdzah
,
H.
, and
Lee
,
H. L.
,
1994
, “
The Effect of Sliding Velocity on the Friction and Wear of UHMWPE for Use in Total Artificial Joints
,”
Wear
,
175
, pp.
219
225
.
25.
Cornwall
,
G. B.
,
Bryant
,
J. T.
,
Hansson
,
C. M.
,
Rudan
,
J.
,
Kennedy
,
L. A.
, and
Cooke
,
T. D.
,
1995
, “
A Quantitative Technique For Reporting Surface Degradation Patterns Of UHMWPE Components Of Retrieved Total Knee Replacements
,”
Journal of Applied Biomaterials
,
6
, pp.
9
18
.
26.
Sutula
,
L. C.
,
Collier
,
J. P.
,
Saum
,
K. A.
,
Currier
,
B. H.
,
Currier
,
J. H.
,
Sanford
,
W. F.
,
Mayor
,
M. B.
,
Wooding
,
R. E.
,
Sperling
,
D. K.
,
Williams
,
I. R.
,
Kasprzak
,
D. J.
, and
Surprenant
,
V. A.
,
1995
, “
Impact of Gamma Sterilization on Clinical Performance of Polyethylene in the Hip
,”
Clin. Orthop. Relat. Res.
,
319
, pp.
28
40
.
27.
Burgess
,
I. C.
,
Kolar
,
M.
,
Cunningham
,
J. L.
, and
Unsworth
,
A.
,
1997
, “
Development of a Six Station Knee Wear Simulator and Preliminary Wear Results
,”
Proc. Inst. Mech. Eng.
,
211
, pp.
37
47
.
28.
Currier
,
J. H.
,
Duda
,
J. L.
,
Sperling
,
D. K.
,
Collier
,
J. P.
,
Currier
,
B. H.
, and
Kennedy
,
F. E.
,
1998
, “
In Vitro Simulation of Contact Fatigue Damage Found in Ultra-High Molecular Weight Polyethylene Components of Knee Prostheses
,”
Proc. Inst. Mech. Eng.
,
212
, pp.
293
302
.
29.
Keller
,
T. S.
,
Weisberger
,
A. M.
,
Ray
,
J. L.
,
Hasan
,
S. S.
,
Shiavi
,
R. G.
, and
Spengler
,
D. M.
,
1996
, “
Relationship Between Vertical Ground Reaction Force and Speed During Walking, Slow Jogging, and Running
,”
Clinical Biomechanics
,
11
, pp.
253
259
.
30.
Andrews
,
E. H.
,
1972
, “
The Influence of Morphology on the Mechanical Properties of Crystalline Polymers
,”
Pure Appl. Chem.
,
31
, pp.
91
109
.
31.
Bhateja
,
S. K.
,
Andrews
,
E. H.
, and
Yarbrough
,
S. M.
,
1989
, “
Radiation Induced Crystallinity Changes in Linear Polyethylenes: Long Term Aging Effects
,”
Polymer
,
21
, pp.
739
750
.
32.
Rimnac
,
C. M.
,
Klein
,
R. W.
,
Betts
,
F.
, and
Wright
,
T. M.
,
1994
, “
Post-irradiation Aging of Ultra-high Molecular Weight Polyethylene
,”
J. Bone Jt. Surg.
,
76-A
, pp.
1052
1056
.
33.
Hertzberg, R. W., and Manson, 1980, “Fatigue Crack Propagation,” in Fatigue of Engineering Plastics, Academic Press, New York, pp. 74–145.
34.
Pruitt
,
L.
, and
Ranganathan
,
R.
,
1995
, “
Effect of sterilization on the structure and fatigue resistance of medical grade UHMWPE
,”
Mater. Sci. Eng., C
,
3
, pp.
91
93
.
35.
Bell
,
C. J.
,
Walker
,
P. S.
,
Abeysundera
,
M. R.
,
Simmons
,
J. M.
,
King
,
P. M.
, and
Blunn
,
G. W.
,
1998
, “
Effect of Oxidation on Delamination of Ultrahigh-molecular-weight Polyethylene Tibial Components
,”
Journal of Arthroplasty
,
13
, pp.
280
290
.
36.
Hamilton, J. V., Wang, H. C., and Sung, C., 1996, “The Effect of Fusion Defects on Mechanical Properties of UHMWPE,” Transactions of the 5th World Biomaterials Congress, University of Toronto Press, Toronto, Canada, Vol. 2, p. 511.
37.
Sevo, K. L., Richelsoph, K. C., Haggard, W. O., Lucas, L. C., Lemons, J. E., and Trieu, H. H., 1999, “Interactive Effect of Calcium Stearate, Supplier Process, Sterilization, and Accelerated Aging on UHMWPE,” Transactions of the Society for Biomaterials, Society for Biomaterials, Minneapolis, MN, Vol. 22, p. 504.
38.
Swarts, D., Gsell, R., King, R., Devanathan, D., Wallace, S., Lin, S., and Rohr, W., 1996, “Aging of Calcium Stearate-Free Polyethylene,” Transactions of the 5th World Biomaterials Congress, University of Toronto Press, Toronto, Canada, Vol. 2, p. 196.
39.
Schmidt, M. B., and Hamilton, J. V., 1996, “The Effects of Calcium on the Properties of UHMWPE,” Transactions of the 42nd Annual Meeting of the Orthopaedic Research Society, Orthopaedic Research Society, Palatine, IL, Vol. 21, p. 22.
40.
McKellop, H., Shen, F. W., Ota, T., Lu, B., Wiser, H., and Yu, E., 1997, “The Effect of Sterilization Method, Calcium Stearate and Molecular Weight on Wear of UHMWPE Acetabular Cups,” Transactions of the Society for Biomaterials, Society for Biomaterials, Minneapolis, MN, Vol. 20, p. 43.
41.
Sauer, W. L., Johnson, R. A., Cooper, M. B., Schwartz, P. A., Wood, C. M., and Weaver, K. D., 1999, “Effects of Calcium Stearate, Consolidation Method, and Consolidation Manufacturer on Physical Properties and Hip Simulator Wear of UHMWPE,” Transactions of the Society for Biomaterials, Society for Biomaterials, Minneapolis, MN, Vol. 22, p. 1.
42.
Rose
,
R. M.
,
Cimino
,
W. R.
,
Ellis
,
E.
, and
Crugnola
,
A. N.
,
1982
, “
Exploratory Investigations on the Structure Dependence of the Wear Resistance of Polyethylene
,”
Wear
,
77
, pp.
89
104
.
43.
Hamilton, J. V., Schmidt, M. B., and Shah, C., 1997. “The Effects of Sterilization Dose on UHMWPE Wear Rates,” Transactions of the 43th Annual Meeting of the Orthopaedic Research Society, Orthopaedic Research Society, Palatine, IL, Vol. 22, p. 782.
You do not currently have access to this content.