The friction and wear properties of unmodified ultra-high molecular weight polyethylene (UHMWPE) were investigated experimentally. Dinks of semicrystalline UHMWPE were slid against polished CoCrWNi pins in bovine serum at ranges of contact pressure and sliding speed typical of those encountered in total joint replacements. The coefficient of friction was monitored continuously during testing, and the wear rate was determined from surface profilometry measurements of worn disk surfaces accounting for strain relaxation. Scanning electron microscopy (SEM) results demonstrated that surface deterioration comprises adhesion, third-body abrasion by polyethylene wear debris, and delamination wear. The contribution of these mechanisms to the overall wear rate and the formation of wear debris depends predominantly on the contact pressure and secondarily on the sliding speed. Transmission electron microscopy (TEM) yielded new insight into the evolution of the microstructure morphology of UHMWPE during sliding. Cross sections parallel to the wear tracks obtained from various depths were analyzed with the TEM to develop a spatial mapping of the subsurface microstructure as a function of contact pressure. Alignment of crystalline regions (lamellae) in the polyethylene microstructure parallel to the sliding surface was found to occur during sliding even at relatively low contact pressures. SEM observations suggested that the highly oriented microstructure is the precursor to delamination wear, leading to the formation of wear particles larger than those produced by adhesion and third-body abrasion at the contact interface.
Skip Nav Destination
Article navigation
April 1999
Research Papers
Tribological Properties and Microstructure Evolution of Ultra-High Molecular Weight Polyethylene
C. Klapperich,
C. Klapperich
Department of Mechanical Engineering, University of California, Berkeley, CA 94720
Search for other works by this author on:
K. Komvopoulos,
K. Komvopoulos
Department of Mechanical Engineering, University of California, Berkeley, CA 94720
Search for other works by this author on:
L. Pruitt
L. Pruitt
Department of Mechanical Engineering, University of California, Berkeley, CA 94720
Search for other works by this author on:
C. Klapperich
Department of Mechanical Engineering, University of California, Berkeley, CA 94720
K. Komvopoulos
Department of Mechanical Engineering, University of California, Berkeley, CA 94720
L. Pruitt
Department of Mechanical Engineering, University of California, Berkeley, CA 94720
J. Tribol. Apr 1999, 121(2): 394-402 (9 pages)
Published Online: April 1, 1999
Article history
Received:
January 15, 1998
Revised:
May 14, 1998
Online:
January 24, 2008
Citation
Klapperich, C., Komvopoulos, K., and Pruitt, L. (April 1, 1999). "Tribological Properties and Microstructure Evolution of Ultra-High Molecular Weight Polyethylene." ASME. J. Tribol. April 1999; 121(2): 394–402. https://doi.org/10.1115/1.2833952
Download citation file:
Get Email Alerts
Related Articles
Tribological and Nanomechanical Properties of Unmodified and Crosslinked Ultra-High Molecular Weight Polyethylene for Total Joint Replacements
J. Tribol (April,2004)
Experimental and Computational Thermal Modeling of In Vitro Pin-on-Disk Tests of Ultra High Molecular Weight Polyethylene
J. Tribol (October,2016)
Related Proceedings Papers
Related Chapters
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies
Contact Laws
Contact in Structural Mechanics: A Weighted Residual Approach
The Tribological Character of LB Films of Dipalmitoylphosphatidylcholine (DPPC)
International Conference on Mechanical and Electrical Technology, 3rd, (ICMET-China 2011), Volumes 1–3