An experimental study of high-pressure waterjet peening on 7075-T6 aluminum alloy was conducted to investigate the effects of waterjet on high-cycle fatigue life and fatigue crack growth. Unnotched hourglass-shaped circular cross section test specimens were fatigue tested in completely reversed rotating bending to determine fatigue life behavior curves). Single-edge-notched flat tensile test specimens were tested in the tension-tension fatigue crack growth tests to determine fatigue crack propagation behavior versus Surface characteristics and fracture surfaces were evaluated by scanning electron microscopy (SEM). Results show that waterjet peening can increase high-cycle fatigue life, delay fatigue crack initiation, and decrease the rate of fatigue crack propagation.
Skip Nav Destination
e-mail: ramulum@u.washington.edu
Article navigation
February 2002
Technical Papers
Fatigue Performance of High-Pressure Waterjet-Peened Aluminum Alloy
M. Ramulu, Fellow ASME,
e-mail: ramulum@u.washington.edu
M. Ramulu, Fellow ASME
Department of Mechanical Engineering, University of Washington, Seattle, WA 98195
Search for other works by this author on:
S. Kunaporn,
S. Kunaporn
Department of Mechanical Engineering, University of Washington, Seattle, WA 98195
Search for other works by this author on:
M. Jenkins,
M. Jenkins
Department of Mechanical Engineering, University of Washington, Seattle, WA 98195
Search for other works by this author on:
M. Hashish, Fellow ASME,
M. Hashish, Fellow ASME
Flow International Corporation, Kent, WA 98032
Search for other works by this author on:
J. Hopkins
J. Hopkins
Flow International Corporation, Kent, WA 98032
Search for other works by this author on:
M. Ramulu, Fellow ASME
Department of Mechanical Engineering, University of Washington, Seattle, WA 98195
e-mail: ramulum@u.washington.edu
S. Kunaporn
Department of Mechanical Engineering, University of Washington, Seattle, WA 98195
M. Jenkins
Department of Mechanical Engineering, University of Washington, Seattle, WA 98195
M. Hashish, Fellow ASME
Flow International Corporation, Kent, WA 98032
J. Hopkins
Flow International Corporation, Kent, WA 98032
Contributed by the Pressure Vessels and Piping Division and presented at the Pressure Vessels Piping Conference, Seattle, Washington, July 23–27, of THE AMERICAN SOCIETY OF MECHANICAL ENGINEERS. Manuscript received by the PVP Division, January 14, 2001; revised manuscript received May 22, 2001. Editor: S. Y. Zamrik.
J. Pressure Vessel Technol. Feb 2002, 124(1): 118-123 (6 pages)
Published Online: May 22, 2001
Article history
Received:
January 14, 2001
Revised:
May 22, 2001
Citation
Ramulu, M., Kunaporn , S., Jenkins, M., Hashish, M., and Hopkins, J. (May 22, 2001). "Fatigue Performance of High-Pressure Waterjet-Peened Aluminum Alloy ." ASME. J. Pressure Vessel Technol. February 2002; 124(1): 118–123. https://doi.org/10.1115/1.1398553
Download citation file:
Get Email Alerts
Measurement of Steam-Generator-Tube Vibration Damping Caused by Anti-Vibration-Bar Supports
J. Pressure Vessel Technol (February 2025)
Related Articles
Effect of Forging Force on Fatigue Behavior of Spot Welded Joints of Aluminum Alloy 5182
J. Manuf. Sci. Eng (February,2007)
Microstructural Characterization of Ultrasonically Welded Aluminum
J. Eng. Mater. Technol (January,2005)
Investigation of Creep/Fatigue Interaction on Crack Growth in a Titanium Aluminide Alloy
J. Eng. Mater. Technol (October,1990)
Effect of Shot Peening Process on the Fatigue Life of Shot Peened Low Alloy Steel
J. Eng. Mater. Technol (January,2018)
Related Proceedings Papers
Related Chapters
Relationship Between Fatigue Crack Growth Behavior and Susceptibility to Hydrogen Embrittlement in 7000 Series Aluminum Alloys
International Hydrogen Conference (IHC 2016): Materials Performance in Hydrogen Environments
Introductory Information
The Stress Analysis of Cracks Handbook, Third Edition
Understanding the Problem
Design and Application of the Worm Gear