Abstract

Many power generation facilities equipped with turbomachinery are designed to provide electric energy on an as-needed basis and, as a consequence, impart a mixture of fatigue and creep damage to high-value components at elevated temperatures. Cracks are often initiated on free surfaces of these parts near stress-raising features and propagate under thermal-mechanical cycling until the component is removed from service. Whether the emphasis is on creep or fatigue failure, most conventional structural life prediction approaches decouple crack initiation from crack propagation. Turbine designers are in need of approaches that span the full life cycle of components in which both initiation and propagation are the consequences of a variety of mechanical failure modes. Although recent fracture mechanics methods have been developed to account for fatigue- and creep-crack growth, a tacit assumption is that a precrack exists. Another main limitation of these approaches is the small scale yielding assumption, associated with linear elastic fracture mechanics, in which extensive plasticity invalidates such analyses. In this study, utilizing a blunt notch compact tensile specimen, experimental routines involving crack initiation and propagation within a single specimen at elevated temperatures with plastic-inducing loads and hold periods were conducted. Founded on existing elastic and elastic-plastic fracture mechanics (EPFM), a coupled crack initiation and propagation model is presented. Through the use of the EPFM parameter J, the proposed models are observed to accurately predict crack initiation and replicate crack propagation rates based on the imposed experimental conditions. The model is demonstrated on an austenitic stainless steel, type 304, subjected to moderate temperatures in air. Mechanical testing, metallurgical analysis, and analytical modeling allow for a simplified phenomenological life prediction model capable of predicting crack initiation and propagation at elevated temperatures. Consequently, structural analysis of critical locations of components can span the gamut of crack initiation, crack growth, and instability (i.e., total life assessment).

References

1.
Paris
,
P. C.
,
Gomez
,
M. P.
, and
Anderson
,
W. E.
, “
A Rational Analytic Theory of Fatigue
,”
Trends Eng.
, Vol.
13
,
1961
, pp.
9
14
.
2.
Paris
,
P. C.
, “
Fracture Mechanics and Fatigue: A Historical Perspective
,”
Fatigue Fract. Eng. Mater. Struct.
, Vol.
21
(
5
),
1998
, pp.
535
540
. https://doi.org/10.1046/j.1460-2695.1998.00054.x
3.
Rice
,
J. R.
, “
A Path Independent Integral and the Approximate Analysis of Strain Concentration by Notches and Cracks
,”
J. Appl. Mech.
, Vol.
35
,
1968
, pp.
379
386
. https://doi.org/10.1115/1.3601206
4.
Landes
,
J. D.
and
Begley
,
J. A.
, “
A Fracture Mechanics Approach to Creep Crack Growth
,”
Mechanics of Crack Growth, ASTM STP 590
,
Rice
J. R.
and
Paris
P. C.
, Eds.,
ASTM International
,
West Conshohocken, PA
,
1976
, pp.
128
148
.
5.
Saxena
,
A.
,
Williams
,
R. S.
, and
Shih
,
T. T.
, “
A Model for Representing and Predicting the Influence of Hold Time on Fatigue Crack Growth Behavior at Elevated Temperature
,”
Proceedings of Fracture Mechanics: Thirteenth Conference, ASTM STP 743
,
Roberts
R.
, Ed., Philadelphia, PA, June 16–18, 1980,
ASTM International
,
West Conshohocken, PA
,
1981
, pp.
86
99
.
6.
Saxena
,
A.
, “
Creep Crack Growth under Non-Steady-State Conditions
,”
Fracture Mechanics: Seventh Volume, ASTM STP 905
,
Underwood
J. H.
,
Chait
R.
,
Smith
C. W.
,
Wilhem
D. P.
,
Andrews
W. A.
, and
Newman
J. C.
, Eds., Albany, NY, Aug 7–9,
1984
,
ASTM International
,
West Conshohocken, PA
,
1986
, pp.
185
201
.
7.
Baik
,
Y. M.
and
Kim
,
K. S.
, “
Crack Growth in Stainless Steel 304 Under Creep-Fatigue Loading
,”
Key Eng. Mater.
, Vol.
353
(
1
),
2007
, pp.
485
490
. https://doi.org/10.4028/www.scientific.net/KEM.353-358.485
8.
Zhang
,
G.
,
Yuan
,
H.
, and
Li
,
F.
, “
Analysis of Creep-Fatigue Life Prediction Models for Nickel-based Super Alloys
,”
Comput. Mater. Sci.
, Vol.
57
,
2012
, pp.
80
88
. https://doi.org/10.1016/j.commatsci.2011.07.034
9.
Dowling
,
N. E.
, “
Fatigue at Notches and the Local Strain and Fracture Mechanics Approaches
,”
Fracture Mechanics: Proceedings of the Eleventh National Symposium on Fracture Mechanics: Part I, ASTM STP 677
,
Smith
C. W.
, Ed., Blacksburg, Va., June 12–14, 1978,
ASTM International
,
West Conshohocken, PA
,
1979
, pp.
247
273
.
10.
Benachour
,
N.
,
Hadjoui
,
A.
,
Benachour
,
M.
, and
Benguediab
,
M.
, “
Stress Ratio and Notch Effect on Fatigue Crack Initiation and Propagation in 2024 Al-Alloy
,”
Proc. World Acad. Sci. Eng. Technol.
, Vol.
79
,
2011
, pp.
566
569
.
11.
Lazzarin
,
P.
,
Tovo
,
R.
, and
Meneghetti
,
G.
, “
Fatigue Crack Initiation and Propagation Phases Near Notches in Metals with Low Notch Sensitivity
,”
Int. J. Fatigue
, Vol.
19
(
8–9
),
1997
, pp.
647
657
. https://doi.org/10.1016/S0142-1123(97)00091-1
12.
Furuya
,
Y.
and
Shimada
,
H.
, “
Fatigue Crack Initiation from Notch Root (Local-Strain Damage Accumulation Process on Crack Initiation
,”
Eng. Fract. Mech.
, Vol.
23
(
6
),
1986
, pp.
983
989
. https://doi.org/10.1016/0013-7944(86)90142-6
13.
Leidermark
,
D.
,
Moverare
,
J.
,
Simonsson
,
K.
, and
Sjostrom
,
S.
, “
A Combined Critical Plane and Critical Distance Approach for Predicting Fatigue Crack Initiation in Notched Single-Crystal Superalloy Components
,”
Int. J. Fatigue
, Vol.
33
(
10
),
2011
, pp.
1351
1359
. https://doi.org/10.1016/j.ijfatigue.2011.05.009
14.
Heckel
,
K.
and
Wanger
,
R.
, “
Tensile Fatigue Behavior of C(T)-Specimens with Small Notch Root Radius
,”
Int. J. Fract.
, Vol.
11
(
1
),
1975
, pp.
135
140
. https://doi.org/10.1007/BF00034720
15.
Dowling
,
N. E.
and
Wilson
,
W. K.
, “
Results of Elastic Analysis of Bluntly Notched Compact Specimens
,”
Eng. Fract. Mech.
, Vol.
20
(
3
),
1984
, pp.
569
572
. https://doi.org/10.1016/0013-7944(84)90061-4
16.
Tanaka
,
K.
,
Nakai
,
Y.
, and
Kawashima
,
R.
, “
Fracture Mechanics Approach to Fatigue Crack Initiation from Deep Notches
,”
Eng. Fract. Mech.
, Vol.
18
(
5
),
1983
, pp.
1011
1023
. https://doi.org/10.1016/0013-7944(83)90073-5
17.
Creager
,
M.
and
Paris
,
P. C.
, “
Elastic Field Equations for Blunt Cracks with Reference to Stress Corrosion Cracking
,”
Int. J. Fract. Mech.
, Vol.
3
(
4
),
1967
, pp.
247
252
.
18.
ASTM E399-09ε2
:
Standard Test Methods for Linear-Elastic Plane-Strain Fracture Toughness, Kic, of Metallic Materials
,
Annual Book of ASTM Standards
,
ASTM International
,
West Conshohocken, PA
.
19.
ASTM E647-08ε2
:
Standard Test Method for Measure of Fatigue Crack Growth Rates
,
Annual Book of ASTM Standards
,
ASTM International
,
West Conshohocken, PA
,
2008
.
20.
ASTM E1820-09ε1
:
Standard Test Method for Measurement of Fracture Toughness
,
Annual Book of ASTM Standards
,
ASTM International
,
West Conshohocken, PA
,
2009
.
21.
Keller
,
S. G.
,
2013
, “
Creep-Fatigue Crack Initiation and Propagation of a Notched Stainless Steel
,” Ph.D. dissertation,
University of Central Florida
, Orlando, FL.
22.
ASTM E8/E8M-09
:
Standard Test Method for Tension Testing of Metallic Materials
,
Annual Book of ASTM Standards
,
ASTM International
,
West Conshohocken, PA
,
2009
.
23.
ASTM E21-09
:
Standard Test Methods for Elevated Temperature Tension Tests of Metallic Materials
,
Annual Book of ASTM Standards
,
ASTM International
,
West Conshohocken, PA
,
2009
.
24.
Dowling
,
N. E.
and
Begley
,
J. A.
, “
Fatigue Crack Growth During Gross Plasticity and the J-Integral
,”
Mechanics of Crack Growth, ASTM STP 590
,
Rice
J. R.
and
Paris
P. C.
, Eds.,
ASTM International
,
West Conshohocken, PA
,
1976
, pp.
82
103
.
25.
Forman
,
R. G.
,
Kearney
,
V. E.
, and
Engle
,
R. M.
, “
Numerical Analysis of Crack Propagation in Cyclic-Loaded Structures
,”
J. Basic Eng.
, Vol.
89
(
3
),
1967
, pp.
459
464
. https://doi.org/10.1115/1.3609637
26.
Elber
,
W.
, “
The Significance of Fatigue Crack Closure
,”
Damage Tolerance in Aircraft Structures, ASTM STP 486
,
Paris
P. S.
and
Hebert
R. J.
, Eds.,
ASTM International
,
West Conshohocken, PA
,
1971
, pp.
230
242
.
27.
Yamada
,
Y.
and
Newman
,
J. C.
, “
Crack Closure under High Load-Ratio Conditions for Inconel-718 Near Threshold Behavior
,”
Eng. Fract. Mech.
, Vol.
76
(
2
),
2009
, pp.
209
220
. https://doi.org/10.1016/j.engfracmech.2008.09.009
28.
NASGRO User Manual
,
v6.21.
(
2012
).
Southwest Research Institute
,
San Antonio, Texas
.
This content is only available via PDF.
You do not currently have access to this content.