Abstract

The study investigated the effect of a series of Ca–Mg and a commercial grade MgFeSi graphite nodularizers, Fe75Si, and NiFeSi inoculants on the nodular characteristics (particle size, excursion ratio, degree of sphroidization, nodule count, and shape factor/nodularity) of ductile cast irons produced using a 100 kg diesel fired rotary furnace. This was with a view to controlling the volatile and fading effects of magnesium as a graphite nodularizer in the cast iron melt. Heats of the rotary furnace melts were pre-desulphurized with a pre-determined amount of CaC2:Fe45%Si in ratio 3:1. Subsequently, each melt was treated with different ratios of Ca–Mg based master alloys and the cast irons produced were compared with a commercial grade MgFeSi treated cast iron produced under the same conditions. Post-treatment inoculation in each case was carried out using Fe-75-Si. Microstructural characterization was carried out to determine the graphite nodularity and distribution characteristics. The results showed that the cast iron treated with 1:4 ratio of Ca:Mg combination master alloy yielded the optimum graphite nodularity with ASTM type 1 graphite nodule features, which are comparable to cast irons produced using the commercial grade MgFeSi nodularizer.

Issue Section:
Research Papers
Keywords:
master alloy, graphite nodularizer, ductile iron, nodularity, excursion ratio, shape factor, nodule count

References

1.
Imasogie
,
B. I.
,
Ali
,
J. A.
, and
Afonja
,
A. A.
, “
Properties of As—Cast and Heat Treated Nodular Graphite Cast Irons Melts Treated With CaSi–CaF2 Alloy
,”
Scand. J. Metall.
, Vol.
30
, No.
2
,
2001
, pp.
91
–
102
. https://doi.org/10.1034/j.1600-0692.2001.300206.x
Google Scholar
Crossref
Search ADS
 
2.
Modern Casting
, Report, “
A Modern Casting Staff Report, 34th Annual Census of World Casting Production
,” Modern Casting Report No. 93-96,
AFS
, Schaumburg, IL,
1999
.
3.
Angus
,
H. T.
,
Cast Iron: Physical and Engineering Properties
, 2nd ed.,
Butterworths
,
London
,
1976
.
4.
Arazanbal
,
J.
,
Gutierrez
,
I.
, and
Urcola
,
J. J.
, “
Influence of Heat Treatment on Microstructure of Austempered Ductile Iron
,”
J. Mater. Sci. Technol.
, Vol.
10
, No.
8
,
1994
, pp.
728
–
737
.
Google Scholar
Crossref
Search ADS
 
5.
Atanda
,
P. O.
,
2009
, “
Development of an Integrated Salt Bath Iso-Thermal Heat Treatment Furnace Unit for Austempering of Ductile Iron
,” Ph.D. thesis,
Obafemi Awolowo University
, Ile-Ife, 220005, Nigeria.
6.
Imasogie
,
B. I.
,
2002
, “
SEM Study of Graphite Morphologies in Cast Irons Treated with Calcium-Magnesium Based Master Alloys
,”
Proceedings of the First Nigerian Materials Congress (NIMACON 2002)
, Akure, Ondo State, Nigeria, Nov 11–13,
2002
,
Engineering Materials Development Institute (EMDI)
, pp.
60
–
65
.
7.
Imasogie
,
B. I.
,
Afonja
,
A. A.
, and
Ali
,
J. A.
, “
Properties of Ductile Cast Iron Nodularized with a Multiple Calcium-Magnesium Based Master Alloy
,”
J. Mater. Sci. Eng.
, Vol.
16
, No.
2
,
2000
, pp.
194
–
201
.
8.
Davis
,
K. G.
 and
Magny
,
J. G.
, “
Effect of Hydrogen Charging on Nodularization Efficiency of a Rare-Earth Alloy Used in Treating Cast Iron
,”
Metal. Sci.
, Vol.
12
,
1978
, pp.
51
–
55
.
Google Scholar
Crossref
Search ADS
 
9.
Kurganov
,
V. A.
,
Taran
,
Y. N.
,
Krause
,
L. A.
,
Lesovoi
,
V. V.
, and
Sofonov
,
V. F.
, “
Use of Complex Inoculants in the Production of High Strength Cast Iron Ingot Molds
,”
Liteinoe Proizvod.
, Vol.
1
,
1981
, pp.
8
–
10
.
10.
Krzemien
,
E.
, “
Cast Iron Spheroidization in Casting Mould
,”
Zesz. Nauk. Politech. Slask. [Hutn.]
, Vol.
2
,
1979
, pp.
123
–
130
.
11.
Petrichenko
,
A. M.
,
Priymak
,
V. A.
, and
Mozharov
,
M. V.
, “
Use of Complex Inoculants for the Production of Spheroidal Graphite Cast Iron
,”
Liteinoe Proizvod.
, Vol.
1
,
1981
, pp.
7
–
8
.
12.
Horuichi
,
Y.
, “
Study on the Production of Spheroidal Graphite Cast Iron by Calcium Treatment
,”
Testu to Hagane
, Vol.
43
,
1957
, pp.
903
–
908
.
13.
Olorunniwo
,
O. E.
,
2009
, “
Evaluation of Metallurgical Process Parameters for the Production of Ductile Iron Using a Fuel Fired Rotary Furnace
,” Ph.D. thesis,
Obafemi Awolowo University
, Ile-Ife, 220005, Nigeria.
14.
Franklin
,
S. E.
 and
Stark
,
R. A.
, “
Application of Secondary Ion Mass Spectrometry to Study of Graphite Morphology in Cast Iron
,”
J. Metal. Sci.
, Vol.
18
,
1984
, pp.
187
–
200
. https://doi.org/10.1179/030634584790420186
Google Scholar
Crossref
Search ADS
 
15.
Imasogie
,
B. I.
,
1994
, “
Development and Characterization of Isothermally Heat-Treated Nodular Cast Irons
,” Ph.D. thesis,
Obafemi Awolowo University
, Ile-Ife, Nigeria.
16.
Tanaka
,
Y.
,
Saito
,
H.
,
Tokura
,
I.
, and
Ikawa
,
K.
, “
Relationship Between Some Physico-Mechanical Properties and Numerical Indexes of Graphite Shape in Compacted-Vermicular Graphite Cast Irons
,”
J. Eng. Mater. Technol.
, Vol.
104
, No.
2
,
1984
, pp.
60
–
65
. https://doi.org/10.1115/1.3225037
17.
Umoru
,
L. E.
,
Ali
,
J. A.
, and
Afonja
,
A. A.
, “
Effect of Calcium on the Degree of Nodularization of Graphite in Cast Iron
,”
NSE Technol. Trans.
, Vol.
2
,
2005
, pp.
33
–
42
.
This content is only available via PDF.
All rights reserved. This material may not be reproduced or copied, in whole or part, in any printed, mechanical, electronic, film, or other distribution and storage media, without the written consent of ASTM International.
You do not currently have access to this content.